供应 LLDPE 陶氏 HS-7046 NT 7 塑胶原料
- 起订量 (千克)价格
- 25-1000￥11.8 /千克
- ≥1000￥11.6 /千克
- 品牌：陶氏
- 货号：HS-7046 NT 7
- 发布日期： 2022-07-22
- 更新日期： 2025-09-16
产品详请
| 品牌 | 陶氏 |
| 货号 | HS-7046 NT 7 |
| 用途 | 薄膜 |
| 特性级别 | 耐低温|||高强度|||高抗冲|||高光泽||| |
| 牌号 | HS-7046 NT 7 |
| 型号 | HS-7046 NT 7 |
| 加工级别 | 吹塑级||| |
| 品名 | LLDPE |
| 外形尺寸 | 颗粒 |
| 用途级别 | 通用级|||食品级|||薄膜级|||流延膜专用料|||薄壁制品||| |
| 生产企业 | 陶氏 |
| 是否进口 | 否 |
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 比重 | ASTM D-792 | 0.919 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min | |
| 机械性能 | 电影穿刺能源 | 20.3um | Internal Method | 4.63 | J |
| 50.8um | Internal Method | 6.78 | J | ||
| 电影穿刺力 | 20.3um | Internal Method | 53.4 | N | |
| 50.8um | Internal Method | 84.5 | N | ||
| 电影穿刺抵抗 | 20.3um | Internal Method | 25.2 | J/cm3 | |
| 50.8um | Internal Method | 17.9 | J/cm3 | ||
| 电影韧性(MD) | 20.3um | ASTM D-882 | 303 | J/cm3 | |
| 电影韧性(TD) | 20.3um | ASTM D-882 | 353 | J/cm3 | |
| 电影韧性(MD) | 50.8um | ASTM D-882 | 331 | J/cm3 | |
| 电影韧性(TD) | 50.8um | ASTM D-882 | 361 | J/cm3 | |
| 割线模量-2% Secant(MD) | 20.3um | ASTM D-882 | 196 | MPa | |
| 割线模量-2% Secant(TD) | 20.3um | ASTM D-882 | 221 | MPa | |
| 割线模量-2% Secant(MD) | 50.8um | ASTM D-882 | 196 | MPa | |
| 割线模量-2% Secant(TD) | 50.8um | ASTM D-882 | 219 | MPa | |
| 拉伸屈服强度(MD) | 20.3um | ASTM D-882 | 12.4 | MPa | |
| 拉伸屈服强度(TD) | 20.3um | ASTM D-882 | 13 | MPa | |
| 拉伸屈服强度(MD) | 50.8um | ASTM D-882 | 11.8 | MPa | |
| 拉伸屈服强度(TD) | 50.8um | ASTM D-882 | 14.4 | MPa | |
| 拉伸断裂强度(MD) | 20.3um | ASTM D-882 | 64.8 | MPa | |
| 拉伸断裂强度(TD) | 20.3um | ASTM D-882 | 52.4 | MPa | |
| 拉伸断裂强度(MD) | 50.8um | ASTM D-882 | 54.2 | MPa | |
| 拉伸断裂强度(TD) | 50.8um | ASTM D-882 | 53.6 | MPa | |
| 拉伸断裂伸长率(MD) | 20.3um | ASTM D-882 | 610 | % | |
| 拉伸断裂伸长率(TD) | 20.3um | ASTM D-882 | 860 | % | |
| 拉伸断裂伸长率(MD) | 50.8um | ASTM D-882 | 800 | % | |
| 拉伸断裂伸长率(TD) | 50.8um | ASTM D-882 | 820 | % | |
| 落锤冲击(MD) | 20.3um | ASTM D-1709A | 110 | g | |
| 落锤冲击(TD) | 20.3um | ASTM D-1709B | ＜100 | g | |
| 落锤冲击(MD) | 50.8um | ASTM D-1709A | 350 | g | |
| 落锤冲击(TD) | 50.8um | ASTM D-1709B | 200 | g | |
| 埃尔曼多夫撕裂强度(MD) | 20.3um | ASTM D-1922 | 370 | g | |
| 埃尔曼多夫撕裂强度(TD) | 20.3um | ASTM D-1922 | 700 | g | |
| 埃尔曼多夫撕裂强度(MD) | 50.8um | ASTM D-1922 | 950 | g | |
| 埃尔曼多夫撕裂强度(TD) | 50.8um | ASTM D-1922 | 1300 | g | |
| 密封起始温度 | 20.3um | Internal Method | 110 | ℃ | |
| 50.8um | Internal Method | 120 | ℃ | ||
| 密封强度 | 130℃，0.0203mm | Internal Method | 1000 | g | |
| 150℃，0.0508mm | Internal Method | 2100 | g | ||
| 加工性能 | 熔体温度 | 233 | ℃ | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 104 | ℃ | |
| 熔化温度 | Internal Method | 124 | ℃ | ||
| 光学性能 | 光泽度 | 20°，20.3um | ASTM D-2457 | 87 | |
| 20°，50.8um | ASTM D-2457 | 64 | |||
| 45°，20.3um | ASTM D-2457 | 70 | |||
| 45°，50.8um | ASTM D-2457 | 59 | |||
| 雾度 | 20.3um | ASTM D-1003 | 7 | % | |
| 50.8um | ASTM D-1003 | 14 | % | ||