产品展厅
|
供应 LLDPE 陶氏 HS-7028 NT 7
- 起订量 (千克)价格
- 25-1000￥11.8 /千克
- ≥1000￥11.6 /千克
- 品牌：陶氏
- 货号：HS-7028 NT 7
- 发布日期： 2022-07-22
- 更新日期： 2025-09-16
产品详请
| 品牌 | 陶氏 |
| 货号 | HS-7028 NT 7 |
| 用途 | 薄膜 |
| 特性级别 | 耐低温|||耐老化|||高强度|||高光泽|||高刚性||| |
| 牌号 | HS-7028 NT 7 |
| 型号 | HS-7028 NT 7 |
| 加工级别 | 吹塑级||| |
| 品名 | LLDPE |
| 外形尺寸 | 颗粒 |
| 用途级别 | 通用级|||食品级|||薄膜级|||流延膜专用料|||薄壁制品||| |
| 生产企业 | 陶氏 |
| 是否进口 | 否 |
LLDPE /HS-7028 NT 7 /美国陶氏 物性表技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 比重 | ASTM D-792 | 0.918 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min | |
| 机械性能 | 电影穿刺能源 | 20.3um | Internal Method | 3.39 | J |
| 50.8um | Internal Method | 5.08 | J | ||
| 电影穿刺力 | 20.3um | Internal Method | 40 | N | |
| 50.8um | Internal Method | 71.2 | N | ||
| 电影穿刺抵抗 | 20.3um | Internal Method | 20.9 | J/cm3 | |
| 50.8um | Internal Method | 13 | J/cm3 | ||
| 电影韧性(MD) | 20.3um | ASTM D-882 | 295 | J/cm3 | |
| 电影韧性(TD) | 20.3um | ASTM D-882 | 341 | J/cm3 | |
| 电影韧性(MD) | 50.8um | ASTM D-882 | 253 | J/cm3 | |
| 电影韧性(TD) | 50.8um | ASTM D-882 | 289 | J/cm3 | |
| 割线模量-2% Secant(MD) | 20.3um | ASTM D-882 | 204 | MPa | |
| 割线模量-2% Secant(TD) | 20.3um | ASTM D-882 | 233 | MPa | |
| 割线模量-2% Secant(MD) | 50.8um | ASTM D-882 | 199 | MPa | |
| 割线模量-2% Secant(TD) | 50.8um | ASTM D-882 | 183 | MPa | |
| 拉伸屈服强度(MD) | 20.3um | ASTM D-882 | 16 | MPa | |
| 拉伸屈服强度(TD) | 20.3um | ASTM D-882 | 15.4 | MPa | |
| 拉伸屈服强度(MD) | 50.8um | ASTM D-882 | 12.2 | MPa | |
| 拉伸屈服强度(TD) | 50.8um | ASTM D-882 | 11 | MPa | |
| 拉伸断裂强度(MD) | 20.3um | ASTM D-882 | 60.7 | MPa | |
| 拉伸断裂强度(TD) | 20.3um | ASTM D-882 | 48.2 | MPa | |
| 拉伸断裂强度(MD) | 50.8um | ASTM D-882 | 40.8 | MPa | |
| 拉伸断裂强度(TD) | 50.8um | ASTM D-882 | 46.9 | MPa | |
| 拉伸断裂伸长率(MD) | 20.3um | ASTM D-882 | 580 | % | |
| 拉伸断裂伸长率(TD) | 20.3um | ASTM D-882 | 800 | % | |
| 拉伸断裂伸长率(MD) | 50.8um | ASTM D-882 | 700 | % | |
| 拉伸断裂伸长率(TD) | 50.8um | ASTM D-882 | 850 | % | |
| 落锤冲击(MD) | 20.3um | ASTM D-1709A | 94 | g | |
| 落锤冲击(TD) | 20.3um | ASTM D-1709B | ＜100 | g | |
| 落锤冲击(MD) | 50.8um | ASTM D-1709A | 130 | g | |
| 落锤冲击(TD) | 50.8um | ASTM D-1709B | 270 | g | |
| 埃尔曼多夫撕裂强度(MD) | 20.3um | ASTM D-1922 | 300 | g | |
| 埃尔曼多夫撕裂强度(TD) | 20.3um | ASTM D-1922 | 670 | g | |
| 埃尔曼多夫撕裂强度(MD) | 50.8um | ASTM D-1922 | 820 | g | |
| 埃尔曼多夫撕裂强度(TD) | 50.8um | ASTM D-1922 | 1200 | g | |
| 密封起始温度 | 20.3um | Internal Method | 110 | ℃ | |
| 50.8um | Internal Method | 120 | ℃ | ||
| 密封强度 | 150℃，0.0203mm | Internal Method | 1000 | g | |
| 150℃，0.0508mm | Internal Method | 2100 | g | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 103 | ℃ | |
| 熔化温度 | Internal Method | 124 | ℃ | ||
| 光学性能 | 光泽度 | 20°，20.3um | ASTM D-2457 | 62 | |
| 20°，50.8um | ASTM D-2457 | 90 | |||
| 45°，20.3um | ASTM D-2457 | 50 | |||
| 45°，50.8um | ASTM D-2457 | 61 | |||
| 雾度 | 20.3um | ASTM D-1003 | 12 | % | |
| 50.8um | ASTM D-1003 | 18 | % | ||