| 品牌 | 陶氏 |
| 货号 | HSE-1003 NT 7 |
| 用途 | 流延薄膜 |
| 特性级别 | 增韧级|||透明级|||耐高温|||高滑动|||高光泽||| |
| 牌号 | HSE-1003 NT 7 |
| 型号 | HSE-1003 NT 7 |
| 加工级别 | 吹塑级||| |
| 品名 | LLDPE |
| 外形尺寸 | 颗粒 |
| 厂家 | 陶氏 |
| 用途级别 | 通用级|||食品级|||薄膜级|||流延膜专用料||| |
| 是否进口 | 否 |
LLDPE /HSE-1003 NT 7 /美国陶氏 物性表
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 比重 | ASTM D-792 | 0.918 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 2.5 | g/10min | |
| 机械性能 | 电影穿刺能源 | 20.3um | Internal Method | 3.84 | J |
| 50.8um | Internal Method | 8.25 | J | ||
| 电影穿刺力 | 20.3um | Internal Method | 40 | N | |
| 50.8um | Internal Method | 84.5 | N | ||
| 电影穿刺抵抗 | 20.3um | Internal Method | 26.4 | J/cm3 | |
| 50.8um | Internal Method | 20.8 | J/cm3 | ||
| 电影韧性(MD) | 20.3um | ASTM D-882 | 209 | J/cm3 | |
| 电影韧性(TD) | 20.3um | ASTM D-882 | 269 | J/cm3 | |
| 电影韧性(MD) | 50.8um | ASTM D-882 | 255 | J/cm3 | |
| 电影韧性(TD) | 50.8um | ASTM D-882 | 334 | J/cm3 | |
| 割线模量-2% Secant(MD) | 20.3um | ASTM D-882 | 147 | MPa | |
| 割线模量-2% Secant(TD) | 20.3um | ASTM D-882 | 156 | MPa | |
| 割线模量-2% Secant(MD) | 50.8um | ASTM D-882 | 142 | MPa | |
| 割线模量-2% Secant(TD) | 50.8um | ASTM D-882 | 142 | MPa | |
| 拉伸屈服强度(MD) | 20.3um | ASTM D-882 | 11.2 | MPa | |
| 拉伸屈服强度(TD) | 20.3um | ASTM D-882 | 10.5 | MPa | |
| 拉伸屈服强度(MD) | 50.8um | ASTM D-882 | 10.2 | MPa | |
| 拉伸屈服强度(TD) | 50.8um | ASTM D-882 | 9.98 | MPa | |
| 拉伸断裂强度(MD) | 20.3um | ASTM D-882 | 49.8 | MPa | |
| 拉伸断裂强度(TD) | 20.3um | ASTM D-882 | 36.1 | MPa | |
| 拉伸断裂强度(MD) | 50.8um | ASTM D-882 | 38.4 | MPa | |
| 拉伸断裂强度(TD) | 50.8um | ASTM D-882 | 44.2 | MPa | |
| 拉伸断裂伸长率(MD) | 20.3um | ASTM D-882 | 520 | % | |
| 拉伸断裂伸长率(TD) | 20.3um | ASTM D-882 | 830 | % | |
| 拉伸断裂伸长率(MD) | 50.8um | ASTM D-882 | 720 | % | |
| 拉伸断裂伸长率(TD) | 50.8um | ASTM D-882 | 900 | % | |
| 落锤冲击(MD) | 20.3um | ASTM D-1709A | 130 | g | |
| 落锤冲击(TD) | 20.3um | ASTM D-1709B | ＜100 | g | |
| 落锤冲击(MD) | 50.8um | ASTM D-1709A | 270 | g | |
| 落锤冲击(TD) | 50.8um | ASTM D-1709B | 170 | g | |
| 埃尔曼多夫撕裂强度(MD) | 20.3um | ASTM D-1922 | 180 | g | |
| 埃尔曼多夫撕裂强度(TD) | 20.3um | ASTM D-1922 | 620 | g | |
| 埃尔曼多夫撕裂强度(MD) | 50.8um | ASTM D-1922 | 780 | g | |
| 埃尔曼多夫撕裂强度(TD) | 50.8um | ASTM D-1922 | 1100 | g | |
| 断裂拉伸 | 0.0203mm | Internal Method | 330 | % | |
| 0.0508mm | Internal Method | 520 | % | ||
| 加工性能 | 熔体温度 | 274 | ℃ | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 98.9 | ℃ | |
| 熔化温度 | Internal Method | 124 | ℃ | ||
| 光学性能 | 光泽度 | 20°，20.3um | ASTM D-2457 | 156 | |
| 20°，50.8um | ASTM D-2457 | 146 | |||
| 45°，20.3um | ASTM D-2457 | 95 | |||
| 45°，50.8um | ASTM D-2457 | 91 | |||
| 雾度 | 20.3um | ASTM D-1003 | 1 | % | |
| 50.8um | ASTM D-1003 | 4 | ℃ | ||