产品详请
| 品牌 | 陶氏 |
| 货号 | HS-7066 NT 7 |
| 用途 | 薄膜 |
| 特性级别 | 增韧级|||抗化学性|||高抗冲|||高光泽||| |
| 牌号 | HS-7066 NT 7 |
| 型号 | HS-7066 NT 7 |
| 加工级别 | 吹塑级||| |
| 品名 | LLDPE |
| 外形尺寸 | 颗粒 |
| 用途级别 | 通用级|||食品级|||薄膜级|||流延膜专用料||| |
| 生产企业 | 陶氏 |
| 是否进口 | 否 |
LLDPE /HS-7066 NT 7 /美国陶氏 物性表
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 比重 | ASTM D-792 | 0.926 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.8 | g/10min | |
| 机械性能 | 电影穿刺能源 | 20.3um | Internal Method | 2.37 | J |
| 50.8um | Internal Method | 5.42 | J | ||
| 电影穿刺力 | 20.3um | Internal Method | 40 | N | |
| 50.8um | Internal Method | 80.1 | N | ||
| 电影穿刺抵抗 | 20.3um | Internal Method | 14.2 | J/cm3 | |
| 50.8um | Internal Method | 13.2 | J/cm3 | ||
| 电影韧性(MD) | 20.3um | ASTM D-882 | 300 | J/cm3 | |
| 电影韧性(TD) | 20.3um | ASTM D-882 | 321 | J/cm3 | |
| 电影韧性(MD) | 50.8um | ASTM D-882 | 348 | J/cm3 | |
| 电影韧性(TD) | 50.8um | ASTM D-882 | 353 | J/cm3 | |
| 割线模量-2% Secant(MD) | 20.3um | ASTM D-882 | 276 | MPa | |
| 割线模量-2% Secant(TD) | 20.3um | ASTM D-882 | 333 | MPa | |
| 割线模量-2% Secant(MD) | 50.8um | ASTM D-882 | 282 | MPa | |
| 割线模量-2% Secant(TD) | 50.8um | ASTM D-882 | 333 | MPa | |
| 拉伸屈服强度(MD) | 20.3um | ASTM D-882 | 16.3 | MPa | |
| 拉伸屈服强度(TD) | 20.3um | ASTM D-882 | 19.7 | MPa | |
| 拉伸屈服强度(MD) | 50.8um | ASTM D-882 | 14.8 | MPa | |
| 拉伸屈服强度(TD) | 50.8um | ASTM D-882 | 16 | MPa | |
| 拉伸断裂强度(MD) | 20.3um | ASTM D-882 | 58.8 | MPa | |
| 拉伸断裂强度(TD) | 20.3um | ASTM D-882 | 43.1 | MPa | |
| 拉伸断裂强度(MD) | 50.8um | ASTM D-882 | 52.9 | MPa | |
| 拉伸断裂强度(TD) | 50.8um | ASTM D-882 | 46 | MPa | |
| 拉伸断裂伸长率(MD) | 20.3um | ASTM D-882 | 600 | % | |
| 拉伸断裂伸长率(TD) | 20.3um | ASTM D-882 | 730 | % | |
| 拉伸断裂伸长率(MD) | 50.8um | ASTM D-882 | 790 | % | |
| 拉伸断裂伸长率(TD) | 50.8um | ASTM D-882 | 850 | % | |
| 落锤冲击(MD) | 20.3um | ASTM D-1709A | 58 | g | |
| 落锤冲击(TD) | 20.3um | ASTM D-1709B | ＜100 | g | |
| 落锤冲击(MD) | 50.8um | ASTM D-1709A | 190 | g | |
| 落锤冲击(TD) | 50.8um | ASTM D-1709B | ＜100 | g | |
| 埃尔曼多夫撕裂强度(MD) | 20.3um | ASTM D-1922 | 180 | g | |
| 埃尔曼多夫撕裂强度(TD) | 20.3um | ASTM D-1922 | 650 | g | |
| 埃尔曼多夫撕裂强度(MD) | 50.8um | ASTM D-1922 | 470 | g | |
| 埃尔曼多夫撕裂强度(TD) | 50.8um | ASTM D-1922 | 1100 | g | |
| 密封起始温度 | 20.3um | Internal Method | 120 | ℃ | |
| 50.8um | Internal Method | 130 | ℃ | ||
| 加工性能 | 熔体温度 | 234 | ℃ | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 113 | ℃ | |
| 熔化温度 | Internal Method | 125 | ℃ | ||
| 光学性能 | 光泽度 | 20°，20.3um | ASTM D-2457 | 66 | |
| 20°，50.8um | ASTM D-2457 | 55 | |||
| 45°，20.3um | ASTM D-2457 | 56 | |||
| 45°，50.8um | ASTM D-2457 | 54 | |||
| 雾度 | 20.3um | ASTM D-1003 | 9 | % | |
| 50.8um | ASTM D-1003 | 16 | % | ||
| 密封强度 | 160℃，0.0203mm | Internal Method | 1300 | g | |
| 180℃，0.0508mm | Internal Method | 2200 | g | ||