产品展厅
|
现货供应 PA6 东丽 CM1011G-30 30%玻纤增强
- 品牌：东丽
- 货号：CM1011G-30
- 价格： ￥18/千克
- 发布日期： 2022-09-06
- 更新日期： 2025-12-19
产品详请
| 品牌 | 东丽 |
| 货号 | CM1011G-30 |
| 用途 | 通用级 |
| 牌号 | CM1011G-30 |
| 型号 | CM1011G-30 |
| 品名 | PA6 |
| 外形尺寸 | 颗粒 |
| 厂家 | 东丽 |
| 是否进口 | 否 |
PA6 /CM1011G-30 /日本东丽 物性表
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜1.1 | % |
| 23℃，24小时 | ASTM D-570 | 2.5%水｜- | % | ||
| 物理性能 | 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 无水｜12 | mg/1000次 |
| 1000g,CS-17 | ASTM D-1044 | 2.5%水｜- | mg/1000次 | ||
| 比重 | ASTM D-792 | 无水｜1.12-1.14 | |||
| ASTM D-792 | 2.5%水｜- | ||||
| 机械性能 | IZOD冲击强度 | 23℃，V-缺口1/2 | ASTM D-256 | 无水｜11 | kg.cm/cm |
| 23℃，V-缺口1/2 | ASTM D-256 | 2.5%水｜19 | kg.cm/cm | ||
| 23℃，无缺口1/8 | 无水｜80 | kg.cm/cm | |||
| 23℃，无缺口1/8 | 2.5%水｜100 | kg.cm/cm | |||
| -40℃，V-缺口1/2 | 无水｜8.5 | kg.cm/cm | |||
| -40℃，V-缺口1/2 | 2.5%水｜14 | kg.cm/cm | |||
| -40℃，无缺口1/8 | 无水｜68 | kg.cm/cm | |||
| -40℃，无缺口1/8 | 2.5%水｜79 | kg.cm/cm | |||
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜5 | % | |
| 23℃ | ASTM D-638 | 2.5%水｜5 | % | ||
| 80℃ | ASTM D-638 | 无水｜6 | % | ||
| 80℃ | ASTM D-638 | 2.5%水｜- | % | ||
| -40℃ | ASTM D-638 | 无水｜4.5 | % | ||
| -40℃ | ASTM D-638 | 2.5%水｜- | % | ||
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜2600 | Kg/cm2 | |
| 23℃ | ASTM D-790 | 2.5%水｜1400 | Kg/cm2 | ||
| 80℃ | ASTM D-790 | 无水｜1500 | Kg/cm2 | ||
| 80℃ | ASTM D-790 | 2.5%水｜1000 | Kg/cm2 | ||
| -40℃ | ASTM D-790 | 无水｜3100 | Kg/cm2 | ||
| -40℃ | ASTM D-790 | 2.5%水｜3000 | Kg/cm2 | ||
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜890 | Kg/cm2 | |
| 23℃ | ASTM D-732 | 2.5%水｜700 | Kg/cm2 | ||
| 80℃ | ASTM D-792 | 无水｜7000 | Kg/cm2 | ||
| 80℃ | ASTM D-792 | 2.5%水｜520 | Kg/cm2 | ||
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜120 | R-标度 | |
| 23℃ | ASTM D-785 | 2.5%水｜- | R-标度 | ||
| 23℃ | ASTM D-785 | 无水｜93 | M-标度 | ||
| 23℃ | ASTM D-785 | 2.5%水｜- | M-标度 | ||
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜1700 | Kg/cm2 | |
| 23℃ | ASTM D-638 | 2.5%水｜1050 | Kg/cm2 | ||
| 80℃ | ASTM D-638 | 无水｜1000 | Kg/cm2 | ||
| 80℃ | ASTM D-638 | 2.5%水｜700 | Kg/cm2 | ||
| -40 | ASTM D-638 | 无水｜2550 | Kg/cm2 | ||
| -40 | ASTM D-638 | 2.5%水｜2300 | Kg/cm2 | ||
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜80000 | Kg/cm2 | |
| 23℃ | ASTM D-790 | 2.5%水｜48000 | Kg/cm2 | ||
| 80℃ | ASTM D-790 | 无水｜43000 | Kg/cm2 | ||
| 80℃ | ASTM D-790 | 2.5%水｜34000 | Kg/cm2 | ||
| -40℃ | ASTM D-790 | 无水｜108000 | Kg/cm2 | ||
| -40℃ | ASTM D-790 | 2.5%水｜90000 | Kg/cm2 | ||
| 压缩强度 | 23℃ | ASTM D-695 | 无水｜1800 | Kg/cm2 | |
| 23℃ | ASTM D-695 | 2.5%水｜- | Kg/cm2 | ||
| 80℃ | ASTM D-695 | 无水｜970 | Kg/cm2 | ||
| 80℃ | ASTM D-695 | 2.5%水｜- | Kg/cm2 | ||
| -40℃ | ASTM D-695 | 无水｜2500 | Kg/cm2 | ||
| -40℃ | ASTM D-695 | 2.5%水｜- | Kg/cm2 | ||
| 电气性能 | 体积电阻率 | ASTM D-257 | 无水｜10<sup>15</sup> | Ω.cm | |
| ASTM D-257 | 2.5%水｜10<sup>12</sup> | Ω.cm | |||
| 抗电弧性 | 1/8" | ASTM D-495 | 无水｜131 | 秒 | |
| 1/8" | ASTM D-495 | 2.5%水｜137 | 秒 | ||
| 损耗因素 | 10<sup>3</sup>Hz | ASTM D-150 | 无水｜0.03 | ||
| 10<sup>3</sup>Hz | ASTM D-150 | 2.5%水｜0.18 | |||
| 50Hz | ASTM D-150 | 无水｜0.03 | |||
| 50Hz | ASTM D-150 | 2.5%水｜0.17 | |||
| 介电强度 | 1/8" | ASTM D-149 | 无水｜20 | KV/mm | |
| 1/8" | ASTM D-149 | 2.5%水｜18 | KV/mm | ||
| 介电常数 | 10<sup>3</sup>Hz | ASTM D-150 | 无水｜4.6 | ||
| 10<sup>3</sup>Hz | ASTM D-150 | 2.5%水｜7.9 | |||
| 50HZ | ASTM D-150 | 无水｜4.9 | |||
| 50HZ | ASTM D-150 | 2.5%水｜10.7 | |||
| 10<sup>6</sup>Hz | ASTM D-150 | 无水｜4.0 | |||
| 10<sup>6</sup>Hz | ASTM D-150 | 2.5%水｜4.3 | |||
| 热性能 | 导热系数 | 无水｜0.23 | Kcal/m.hr.°C | ||
| 2.5%水｜- | Kcal/m.hr.°C | ||||
| 线性热膨胀系数 | ASTM D-696 | 无水｜2-3 | 10<sup>-5</sup>cm/cm.℃ | ||
| ASTM D-696 | 2.5%水｜- | ||||
| 比热 | 无水｜0.32 | Cal/g.°C | |||
| 2.5%水｜- | Cal/g.°C | ||||
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 无水｜215 | ℃ | |
| 18.6kg/cm2 | ASTM D-648 | 2.5%水｜- | ℃ | ||
| 熔点 | 差示扫描测热计DSC法 | 无水｜225 | ℃ | ||
| 差示扫描测热计DSC法 | 2.5%水｜- | ℃ | |||
| UL-94抗燃级 | UL 94 | 无水｜HB(1/16") | |||
| UL 94 | 2.5%水｜- | ||||
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 无水｜224 | ℃ | |
| 4.6kg/cm2 | ASTM D-648 | 2.5%水｜- | ℃ | ||
| 其它性能 | 强化含量 | 无水｜30 | WT% | ||
| 2.5%水｜- | WT% | ||||