PA6 /CM1011G-45 /日本东丽 物性表
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 23℃，24hr | ASTM D-570 | 无水｜0.9 | % |
| 23℃，24hr | ASTM D-570 | 1.9%水｜- | % | ||
| 23℃ | ASTM D-570 | 无水｜5.3 | % | ||
| 23℃ | ASTM D-570 | 1.9%水｜- | % | ||
| 物理性能 | 比重 | ASTM D-792 | 无水｜1.50 | ||
| ASTM D-792 | 1.9%水｜- | ||||
| 机械性能 | 断裂伸长率 | -40℃ | ASTM D-638 | 无水｜4.5 | % |
| -40℃ | ASTM D-638 | 1.9%水｜4.5 | % | ||
| 弯曲模量 | 23℃ | ASTM D-790 | 无水｜12.0 | GPa | |
| 23℃ | ASTM D-790 | 1.9%水｜7.1 | GPa | ||
| IZOD缺口冲击强度 | -40℃ | ASTM D-256 | 无水｜125 | J/m | |
| -40℃ | ASTM D-256 | 1.9%水｜145 | J/m | ||
| 弯曲模量 | 80℃ | ASTM D-790 | 无水｜6.2 | GPa | |
| 80℃ | ASTM D-790 | 1.9%水｜4.4 | GPa | ||
| 拉伸屈服强度 | 23℃ | ASTM D-638 | 无水｜205 | MPa | |
| 23℃ | ASTM D-638 | 1.9%水｜130 | MPa | ||
| 弯曲模量 | -40℃ | ASTM D-790 | 无水｜14.0 | GPa | |
| -40℃ | ASTM D-790 | 1.9%水｜12.5 | GPa | ||
| 弯曲强度 | 23℃ | ASTM D-790 | 无水｜290 | MPa | |
| 23℃ | ASTM D-790 | 1.9%水｜180 | MPa | ||
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜5.0 | % | |
| 23℃ | ASTM D-638 | 1.9%水｜5.0 | |||
| 拉伸屈服强度 | 80℃ | ASTM D-638 | 无水｜120 | MPa | |
| 80℃ | ASTM D-638 | 1.9%水｜85 | MPa | ||
| IZOD无缺口冲击强度 | 23℃ | ASTM D-256 | 无水｜100 | KJ/m2 | |
| 23℃ | ASTM D-256 | 1.9%水｜120 | KJ/m2 | ||
| 弯曲强度 | -40℃ | ASTM D-790 | 无水｜330 | MPa | |
| -40℃ | ASTM D-790 | 1.9%水｜280 | MPa | ||
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 无水｜155 | J/m | |
| 23℃ | ASTM D-256 | 1.9%水｜195 | J/m | ||
| 抗压强度 | -40℃ | ASTM D-695 | 无水｜260 | MPa | |
| -40℃ | ASTM D-695 | 1.9%水｜220 | MPa | ||
| 23℃ | ASTM D-695 | 无水｜190 | MPa | ||
| 23℃ | ASTM D-695 | 1.9%水｜120 | MPa | ||
| 80℃ | ASTM D-695 | 无水｜100 | MPa | ||
| 80℃ | ASTM D-695 | 1.9%水｜70 | MPa | ||
| 剪切强度 | 23℃ | ASTM D-732 | 无水｜95 | MPa | |
| 23℃ | ASTM D-732 | 1.9%水｜75 | MPa | ||
| 断裂伸长率 | 80℃ | ASTM D-638 | 无水｜8.0 | % | |
| 80℃ | ASTM D-638 | 1.9%水｜8.0 | % | ||
| 弯曲强度 | 80℃ | ASTM D-790 | 无水｜160 | MPa | |
| 80℃ | ASTM D-790 | 1.9%水｜110 | MPa | ||
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜R121,M95 | R Scale | |
| 23℃ | ASTM D-785 | 1.9%水｜- | R Scale | ||
| IZOD无缺口冲击强度 | -40℃ | ASTM D-256 | 无水｜90 | KJ/m2 | |
| -40℃ | ASTM D-256 | 1.9%水｜95 | KJ/m2 | ||
| 拉伸屈服强度 | -40℃ | ASTM D-638 | 无水｜290 | MPa | |
| -40℃ | ASTM D-638 | 1.9%水｜250 | MPa | ||
| 热性能 | 热导率 | 无水｜0.40 | W/m℃ | ||
| 1.9%水｜- | W/m℃ | ||||
| 线性热膨胀系数 | ASTM D-696 | 无水｜2-3 | 10<sup>-5</sup>/℃ | ||
| ASTM D-696 | 1.9%水｜- | 10<sup>-5</sup>/℃ | |||
| 比热 | 无水｜1.4 | J/p℃ | |||
| 1.9%水｜- | J/p℃ | ||||
| 熔点 | DSC | 无水｜225 | ℃ | ||
| DSC | 1.9%水｜- | ℃ | |||
| 热变形温度 | 0.46MPa | ASTM D-648 | 无水｜225 | ℃ | |
| 0.46MPa | ASTM D-648 | 1.9%水｜- | ℃ | ||
| 1.86MPa | ASTM D-648 | 无水｜215 | ℃ | ||
| 1.86MPa | ASTM D-648 | 1.9%水｜- | ℃ | ||
| 其它性能 | 加强材料 | 无水｜45 | WT% | ||