现货供应 PA6 东丽 CM3001G-45
- 品牌：东丽
- 货号：CM3001G-45
- 价格： ￥18/千克
- 发布日期： 2022-09-06
- 更新日期： 2025-12-19
产品详请
| 品牌 | 东丽 |
| 货号 | CM3001G-45 |
| 用途 | 通用级 |
| 牌号 | CM3001G-45 |
| 型号 | CM3001G-45 |
| 品名 | PA6 |
| 外形尺寸 | 颗粒 |
| 厂家 | 东丽 |
| 是否进口 | 否 |
PA66 /CM3001G-45 /日本东丽 物性表
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜0.4 | % |
| 23℃，24小时 | ASTM D-570 | 1.0%水｜- | % | ||
| 物理性能 | 比重 | ASTM D-792 | 无水｜1.5 | ||
| ASTM D-792 | 1.0%水｜- | ||||
| 机械性能 | 挠曲模量 | -40℃ | ASTM D-790 | 无水｜138000 | Kg/cm2 |
| -40℃ | ASTM D-790 | 1.0%水｜128000 | Kg/cm2 | ||
| IZOD冲击强度 | -40℃，无缺口1/8 | 无水｜85 | kg·cm/cm2 | ||
| -40℃，无缺口1/8 | 1.0%水｜93 | kg·cm/cm2 | |||
| -40℃，V缺口1/2 | ASTM D-256 | 无水｜9.5 | kg·cm/cm | ||
| -40℃，V缺口1/2 | ASTM D-256 | 1.0%水｜10 | kg·cm/cm | ||
| 23℃，无缺口1/8 | 无水｜90 | kg·cm/cm2 | |||
| 23℃，无缺口1/8 | 1.0%水｜100 | kg·cm/cm2 | |||
| 23℃，V缺口1/2 | ASTM D-256 | 无水｜10 | kg·cm/cm | ||
| 23℃，V缺口1/2 | ASTM D-256 | 1.0%水｜14 | kg·cm/cm | ||
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜2150 | Kg/cm2 | |
| 23℃ | ASTM D-638 | 1.0%水｜1700 | Kg/cm2 | ||
| 挠曲强度 | -40℃ | ASTM D-790 | 无水｜3400 | Kg/cm2 | |
| -40℃ | ASTM D-790 | 1.0%水｜3150 | Kg/cm2 | ||
| 压缩强度 | -40℃ | ASTM D-695 | 无水｜2700 | Kg/cm2 | |
| -40℃ | ASTM D-695 | 1.0%水｜- | Kg/cm2 | ||
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 无水｜2150 | Kg/cm2 | |
| 80℃ | ASTM D-638 | 1.0%水｜1700 | Kg/cm2 | ||
| 断裂伸长率 | -40℃ | ASTM D-648 | 无水｜4.5 | % | |
| -40℃ | ASTM D-648 | 1.0%水｜- | % | ||
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜103 | M-标度 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 1.0%水｜- | M-标度 | |
| 23℃ | ASTM D-790 | 无水｜3000 | Kg/cm2 | ||
| 23℃ | ASTM D-790 | 1.0%水｜2500 | Kg/cm2 | ||
| 断裂伸长率 | 80℃ | ASTM D-638 | 无水｜9 | % | |
| 80℃ | ASTM D-638 | 1.0%水｜- | % | ||
| 压缩强度 | 23℃ | ASTM D-695 | 无水｜2000 | Kg/cm2 | |
| 23℃ | ASTM D-695 | 1.0%水｜- | Kg/cm2 | ||
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜5 | % | |
| 23℃ | ASTM D-638 | 1.0%水｜5 | % | ||
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜1050 | Kg/cm2 | |
| 23℃ | ASTM D-732 | 1.0%水｜- | Kg/cm2 | ||
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 无水｜2800 | Kg/cm2 | |
| -40℃ | ASTM D-638 | 1.0%水｜2650 | Kg/cm2 | ||
| 挠曲强度 | 80℃ | ASTM D-790 | 无水｜1950 | Kg/cm2 | |
| 80℃ | ASTM D-790 | 1.0%水｜1650 | Kg/cm2 | ||
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜125000 | Kg/cm2 | |
| 23℃ | ASTM D-790 | 1.0%水｜98000 | Kg/cm2 | ||
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜121 | R-标度 | |
| 23℃ | ASTM D-785 | 1.0%水｜- | R-标度 | ||
| 挠曲模量 | 80℃ | ASTM D-790 | 无水｜81000 | Kg/cm2 | |
| 80℃ | ASTM D-790 | 1.0%水｜65000 | Kg/cm2 | ||
| 压缩强度 | 80℃ | ASTM D-695 | 无水｜1200 | Kg/cm2 | |
| 80℃ | ASTM D-695 | 1.0%水｜- | Kg/cm2 | ||
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜2150 | Kg/cm2 | |
| 23℃ | ASTM D-638 | 1.0%水｜1700 | Kg/cm2 | ||
| 电气性能 | 体积电阻率 | ASTM D-257 | 无水｜10<sup>15</sup> | Ω.cm | |
| ASTM D-257 | 1.0%水｜10<sup>12</sup>-10<sup>13</sup> | Ω.cm | |||
| 介电强度 | 1/8" | ASTM D-149 | 无水｜19 | KV/mm | |
| 1/8" | ASTM D-149 | 1.0%水｜- | KV/mm | ||
| 热性能 | 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 无水｜263 | ℃ |
| 4.6kg/cm2 | ASTM D-648 | 1.0%水｜- | ℃ | ||
| 线性热膨胀系数 | ASTM D-696 | 无水｜2-3 | ×10<sup>-5</sup>cm/cm/℃ | ||
| ASTM D-696 | 1.0%水｜- | ×10<sup>-5</sup>cm/cm/℃ | |||
| 熔点 | 差示扫描测热计DSC | 无水｜265 | ℃ | ||
| 差示扫描测热计DSC | 1.0%水｜- | ℃ | |||
| 比热 | 无水｜0.34 | Cal/g·℃ | |||
| 1.0%水｜- | Cal/g·℃ | ||||
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 无水｜255 | ℃ | |
| 18.6kg/cm2 | ASTM D-648 | 1.0%水｜- | ℃ | ||
| 其它性能 | 强化含量 | 无水｜45 | WT% | ||
| 1.0%水｜- | WT% | ||||