性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
物理性能
|
比重
|
|
ASTMD792
|
1.19
|
g/cm3
|
|
密度
|
|
ISO1183
|
1.20
|
g/cm3
|
|
熔流率（熔体流动速率）(260°C/2.16kg)
|
|
ASTMD1238
|
18
|
g/10min
|
|
溶化体积流率（MVR）(260°C/2.16kg)
|
|
ISO1133
|
15.0
|
cm3/10min
|
|
收缩率-流动(3.20mm)
|
|
InternalMethod
|
0.40to0.60
|
%
|
|
吸水率(饱和,23°C)
|
|
ISO62
|
0.20
|
%
|
|
吸水率(平衡,23°C,50%RH)
|
|
ISO62
|
0.10
|
%
|
|
机械性能
|
拉伸模量2
|
|
ASTMD638
|
2600
|
MPa
|
|
拉伸模量
|
|
ISO527-2/1
|
2600
|
MPa
|
|
抗张强度3(屈服)
|
|
ASTMD638
|
65.0
|
MPa
|
|
拉伸应力(屈服)
|
|
ISO527-2/50
|
65.0
|
MPa
|
|
抗张强度3(断裂)
|
|
ASTMD638
|
58.0
|
MPa
|
|
拉伸应力(断裂)
|
|
ISO527-2/50
|
50.0
|
MPa
|
|
伸长率3(屈服)
|
|
ASTMD638
|
4.1
|
%
|
|
拉伸应变(屈服)
|
|
ISO527-2/50
|
4.0
|
%
|
|
伸长率4(断裂)
|
|
ASTMD638
|
100
|
%
|
|
拉伸应变(断裂)
|
|
ISO527-2/50
|
90
|
%
|
|
弯曲模量4(50.0mm跨距)
|
|
ASTMD790
|
2500
|
MPa
|
|
弯曲模量5
|
|
ISO178
|
2500
|
MPa
|
|
FlexuralStress5,6
|
|
ISO178
|
96.0
|
MPa
|
|
弯曲强度4(屈服,50.0mm跨距)
|
|
ASTMD790
|
104
|
MPa
|
|
冲击性能
|
简支梁缺口冲击强度7
|
-30°C
|
ISO179/1eA
|
10
|
kJ/m2
|
|
23°C
|
ISO179/1eA
|
40
|
kJ/m2
|
|
悬壁梁缺口冲击强度
|
-30°C
|
ASTMD256
|
180
|
J/m
|
|
23°C
|
ASTMD256
|
700
|
J/m
|
|
悬壁梁缺口冲击强度8
|
-30°C
|
ISO180/1A
|
10
|
kJ/m2
|
|
23°C
|
ISO180/1A
|
40
|
kJ/m2
|
|
装有测量仪表的落镖冲击(23°C,TotalEnergy)
|
|
ASTMD3763
|
65.0
|
J
|
|
热性能
|
载荷下热变形温度(1.8MPa,未退火,3.20mm)
|
|
ASTMD648
|
89.0
|
°C
|
|
HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan)
|
|
ISO75-2/Af
|
93.0
|
°C
|
|
维卡软化温度
|
|
ASTMD152510
|
110
|
°C
|
|
--
|
ISO306/B50
|
110
|
°C
|
|
--
|
ISO306/B120
|
113
|
°C
|
|
BallPressureTest(75°C)
|
|
IEC60695-10-2
|
Pass
|
|
|
线形热膨胀系数-流动(-40到40°C)
|
|
ASTME831
|
7.5E-5
|
cm/cm/°C
|
|
|
ISO11359-2
|
7.5E-5
|
cm/cm/°C
|
|
线形热膨胀系数-横向(-40到40°C)
|
|
ASTME831
|
7.5E-5
|
cm/cm/°C
|
|
|
ISO11359-2
|
7.5E-5
|
cm/cm/°C
|
|
RTIElec
|
|
UL746
|
90.0
|
°C
|
|
RTIImp
|
|
UL746
|
90.0
|
°C
|
|
RTIStr
|
|
UL746
|
90.0
|
°C
|
|
电气性能
|
相比耐漏电起痕指数(CTI)
|
|
UL746
|
PLC3
|
|
|
高电弧燃烧指数(HAI)
|
|
UL746
|
PLC0
|
|
|
热丝引燃(HWI)
|
|
UL746
|
PLC3
|
|
|
可燃性
|
UL阻燃等级
|
0.75mm
|
UL94
|
V-0
|
|
|
1.5mm
|
UL94
|
5VB
|
|
|
灼热丝易燃指数(3.0mm)
|
|
IEC60695-2-12
|
960
|
°C
|
|
热灯丝点火温度(3.0mm)
|
|
IEC60695-2-13
|
800
|
°C
|