性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
物理性能
|
SpecificGravity(Natural)
|
|
ASTMD792
|
1.18
|
g/cm3
|
|
密度(本色)
|
|
ISO1183
|
1.18
|
g/cm3
|
|
熔流率（熔体流动速率）(250°C/10.0kg)
|
|
ASTMD1238
|
19
|
g/10min
|
|
|
ISO1133
|
19
|
g/10min
|
|
收缩率-流动(3.20mm)
|
|
ASTMD955
|
0.54to0.66
|
%
|
|
MoldingShrinkage-AcrossFlow(3.20mm)
|
|
ASTMD955
|
0.56to0.69
|
%
|
|
收缩率
|
横向流量:3.20mm
|
ISO2577
|
0.56to0.69
|
%
|
|
流量:3.20mm
|
ISO2577
|
0.54to0.66
|
%
|
|
机械性能
|
拉伸模量2
|
|
ASTMD638
|
1900
|
MPa
|
|
拉伸模量
|
|
ISO527-2/50
|
2100
|
MPa
|
|
抗张强度2(屈服)
|
|
ASTMD638
|
52.0
|
MPa
|
|
拉伸应力(屈服)
|
|
ISO527-2/50
|
55.0
|
MPa
|
|
抗张强度2(断裂)
|
|
ASTMD638
|
61.0
|
MPa
|
|
拉伸应力(断裂)
|
|
ISO527-2/50
|
67.0
|
MPa
|
|
伸长率2(断裂)
|
|
ASTMD638
|
94
|
%
|
|
拉伸应变(断裂)
|
|
ISO527-2/50
|
110
|
%
|
|
弯曲模量3
|
|
ASTMD790
|
2100
|
MPa
|
|
弯曲模量4
|
|
ISO178
|
2100
|
MPa
|
|
弯曲强度3
|
|
ASTMD790
|
75.0
|
MPa
|
|
弯曲应力4
|
|
ISO178
|
80.0
|
MPa
|
|
冲击性能
|
CharpyNotchedImpactStrength5(23°C)
|
|
ISO179/1eA
|
70
|
kJ/m2
|
|
悬壁梁缺口冲击强度
|
23°C,3.18mm
|
ASTMD256
|
710
|
J/m
|
|
23°C,6.35mm
|
ASTMD256
|
540
|
J/m
|
|
悬壁梁缺口冲击强度5(23°C)
|
|
ISO180/1A
|
65
|
kJ/m2
|
|
硬度
|
洛氏硬度(R级)
|
|
ASTMD785
|
118
|
|
|
|
ISO2039-2
|
120
|
|
|
热性能
|
HeatDeflectionTemperature(0.45MPa,Unannealed,4.00mm)
|
|
ISO75-2/B
|
135
|
°C
|
|
HeatDeflectionTemperature(0.45MPa,Annealed,4.00mm)
|
|
ISO75-2/B
|
135
|
°C
|
|
载荷下热变形温度(1.8MPa,未退火,6.40mm)
|
|
ASTMD648
|
129
|
°C
|
|
HeatDeflectionTemperature(1.8MPa,Unannealed,4.00mm)
|
|
ISO75-2/A
|
121
|
°C
|
|
HeatDeflectionTemperature(1.8MPa,Annealed,4.00mm)
|
|
ISO75-2/A
|
123
|
°C
|
|
维卡软化温度
|
--
|
ISO306/B50
|
142
|
°C
|
|
--
|
ISO306/B120
|
145
|
°C
|
|
RTIElec(1.5mm)
|
|
UL746
|
130
|
°C
|
|
RTIImp(1.5mm)
|
|
UL746
|
130
|
°C
|
|
RTIStr(1.5mm)
|
|
UL746
|
130
|
°C
|
|
可燃性
|
UL阻燃等级
|
0.75mm
|
UL94
|
V-2
|
|
|
1.5mm
|
UL94
|
V-0
|
|
|
3.0mm
|
UL94
|
V-0
|