性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
物理性能
|
SpecificGravity(Natural)
|
|
ASTMD792
|
1.09
|
g/cm3
|
|
密度(本色)
|
|
ISO1183
|
1.09
|
g/cm3
|
|
熔流率（熔体流动速率）
|
250°C/10.0kg
|
ASTMD1238
|
31
|
g/10min
|
|
250°C/2.16kg
|
ASTMD1238
|
3.0
|
g/10min
|
|
250°C/10.0kg
|
ISO1133
|
31
|
g/10min
|
|
250°C/2.16kg
|
ISO1133
|
3.0
|
g/10min
|
|
收缩率-流动(3.20mm)
|
|
ASTMD955
|
0.40to0.70
|
%
|
|
MoldingShrinkage-AcrossFlow(3.20mm)
|
|
ASTMD955
|
0.40to0.70
|
%
|
|
收缩率
|
横向流量:3.20mm
|
ISO2577
|
0.40to0.70
|
%
|
|
流量:3.20mm
|
ISO2577
|
0.40to0.70
|
%
|
|
机械性能
|
拉伸模量2
|
|
ASTMD638
|
1900
|
MPa
|
|
拉伸模量
|
|
ISO527-2/50
|
1900
|
MPa
|
|
抗张强度2(屈服)
|
|
ASTMD638
|
49.0
|
MPa
|
|
拉伸应力(屈服)
|
|
ISO527-2/50
|
47.0
|
MPa
|
|
抗张强度2(断裂)
|
|
ASTMD638
|
39.0
|
MPa
|
|
拉伸应力(断裂)
|
|
ISO527-2/50
|
41.0
|
MPa
|
|
伸长率2(断裂)
|
|
ASTMD638
|
100
|
%
|
|
拉伸应变(断裂)
|
|
ISO527-2/50
|
73
|
%
|
|
弯曲模量3
|
|
ASTMD790
|
1900
|
MPa
|
|
弯曲模量4
|
|
ISO178
|
2000
|
MPa
|
|
弯曲强度3
|
|
ASTMD790
|
66.0
|
MPa
|
|
弯曲应力4
|
|
ISO178
|
70.0
|
MPa
|
|
冲击性能
|
CharpyNotchedImpactStrength5(23°C)
|
|
ISO179/1eA
|
47
|
kJ/m2
|
|
悬壁梁缺口冲击强度
|
-30°C,3.18mm
|
ASTMD256
|
390
|
J/m
|
|
-30°C,6.35mm
|
ASTMD256
|
250
|
J/m
|
|
23°C,3.18mm
|
ASTMD256
|
540
|
J/m
|
|
23°C,6.35mm
|
ASTMD256
|
410
|
J/m
|
|
悬壁梁缺口冲击强度5
|
-30°C
|
ISO180/1A
|
35
|
kJ/m2
|
|
23°C
|
ISO180/1A
|
45
|
kJ/m2
|
|
硬度
|
洛氏硬度(R级)
|
|
ASTMD785
|
105
|
|
|
|
ISO2039-2
|
107
|
|
|
热性能
|
载荷下热变形温度(0.45MPa,未退火,6.40mm)
|
|
ASTMD648
|
120
|
°C
|
|
HeatDeflectionTemperature(0.45MPa,Annealed,4.00mm)
|
|
ISO75-2/B
|
116
|
°C
|
|
载荷下热变形温度(1.8MPa,未退火,6.40mm)
|
|
ASTMD648
|
100
|
°C
|
|
HeatDeflectionTemperature(1.8MPa,Annealed,4.00mm)
|
|
ISO75-2/A
|
101
|
°C
|
|
维卡软化温度
|
--
|
ISO306/B50
|
111to113
|
°C
|
|
--
|
ISO306/B120
|
114
|
°C
|
|
CLTE-Flow(40to100°C)
|
|
ASTME831
|
8.5E-5
|
cm/cm/°C
|
|
|
ISO11359-2
|
8.5E-5
|
cm/cm/°C
|