性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
物理性能
|
SpecificGravity(Natural)
|
|
ASTMD792
|
1.17
|
g/cm3
|
|
密度(本色)
|
|
ISO1183
|
1.17
|
g/cm3
|
|
熔流率（熔体流动速率）(200°C/5.0kg)
|
|
ASTMD1238
|
1.6
|
g/10min
|
|
|
ISO1133
|
1.6
|
g/10min
|
|
收缩率-流动(3.20mm)
|
|
ASTMD955
|
0.40to0.49
|
%
|
|
MoldingShrinkage-AcrossFlow(3.20mm)
|
|
ASTMD955
|
0.43to0.53
|
%
|
|
收缩率
|
横向流量:3.20mm
|
ISO2577
|
0.43to0.53
|
%
|
|
流量:3.20mm
|
ISO2577
|
0.40to0.49
|
%
|
|
机械性能
|
拉伸模量2
|
|
ASTMD638
|
1600
|
MPa
|
|
拉伸模量
|
|
ISO527-2/5
|
2450
|
MPa
|
|
抗张强度2(屈服)
|
|
ASTMD638
|
43.0
|
MPa
|
|
拉伸应力(屈服)
|
|
ISO527-2/5
|
45.0
|
MPa
|
|
抗张强度2(断裂)
|
|
ASTMD638
|
31.0
|
MPa
|
|
拉伸应力(断裂)
|
|
ISO527-2/5
|
37.0
|
MPa
|
|
伸长率2(断裂)
|
|
ASTMD638
|
8.0
|
%
|
|
拉伸应变(断裂)
|
|
ISO527-2/5
|
5.0
|
%
|
|
弯曲模量3
|
|
ASTMD790
|
2300
|
MPa
|
|
弯曲模量4
|
|
ISO178
|
2350
|
MPa
|
|
弯曲强度3
|
|
ASTMD790
|
64.0
|
MPa
|
|
弯曲应力4
|
|
ISO178
|
66.0
|
MPa
|
|
冲击性能
|
CharpyNotchedImpactStrength5(23°C)
|
|
ISO179/1eA
|
16
|
kJ/m2
|
|
悬壁梁缺口冲击强度
|
23°C,3.18mm
|
ASTMD256
|
150
|
J/m
|
|
23°C,6.35mm
|
ASTMD256
|
140
|
J/m
|
|
悬壁梁缺口冲击强度5(23°C)
|
|
ISO180/1A
|
14
|
kJ/m2
|
|
硬度
|
洛氏硬度(R级)
|
|
ASTMD785
|
104
|
|
|
|
ISO2039-2
|
104
|
|
|
热性能
|
载荷下热变形温度(0.45MPa,未退火,6.40mm)
|
|
ASTMD648
|
98.0
|
°C
|
|
HeatDeflectionTemperature(0.45MPa,Unannealed,4.00mm)
|
|
ISO75-2/B
|
98.0
|
°C
|
|
载荷下热变形温度(1.8MPa,未退火,6.40mm)
|
|
ASTMD648
|
85.0
|
°C
|
|
HeatDeflectionTemperature(1.8MPa,Unannealed,4.00mm)
|
|
ISO75-2/A
|
85.0
|
°C
|
|
维卡软化温度
|
|
ISO306/B50
|
97.0
|
°C
|
|
可燃性
|
UL阻燃等级
|
1.5mm
|
UL94
|
V-0
|
|
|
2.5to2.7mm
|
UL94
|
V-05VB
|