性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
物理性能
|
比重
|
|
ASTMD792
|
1.41
|
g/cm3
|
|
密度
|
|
ISO1183
|
1.40
|
g/cm3
|
|
收缩率-流量(24小时)
|
|
ASTMD955
|
2.5to3.0
|
%
|
|
MoldingShrinkage-AcrossFlow(24hr)
|
|
ASTMD955
|
2.5to2.7
|
%
|
|
吸水率(24hr,50%RH)
|
|
ASTMD570
|
0.97
|
%
|
|
机械性能
|
拉伸模量2
|
|
ASTMD638
|
2650
|
MPa
|
|
拉伸模量
|
|
ISO527-2/1
|
3050
|
MPa
|
|
抗张强度(屈服)
|
|
ASTMD638
|
51.6
|
MPa
|
|
拉伸应力(屈服)
|
|
ISO527-2
|
53.0
|
MPa
|
|
伸长率(屈服)
|
|
ASTMD638
|
20
|
%
|
|
弯曲模量
|
|
ASTMD790
|
2160
|
MPa
|
|
|
ISO178
|
2260
|
MPa
|
|
弯曲强度
|
|
ASTMD790
|
68.9
|
MPa
|
|
摩擦系数
|
Dynamic
|
ASTMD3702Modified
|
0.30
|
|
|
Static
|
ASTMD3702Modified
|
0.090
|
|
|
磨损因数-Washer
|
|
ASTMD3702Modified
|
12.0
|
10^-10in^5-min/ft-lb-hr
|
|
冲击性能
|
悬壁梁缺口冲击强度(23°C)
|
|
ASTMD256
|
68
|
J/m
|
|
悬壁梁缺口冲击强度3(23°C)
|
|
ISO180/1A
|
5.9
|
kJ/m2
|
|
悬壁梁缺口冲击强度(23°C)
|
|
ASTMD4812
|
1400
|
J/m
|
|
热性能
|
载荷下热变形温度(0.45MPa,未退火,3.20mm)
|
|
ASTMD648
|
157
|
°C
|
|
载荷下热变形温度(1.8MPa,未退火,3.20mm)
|
|
ASTMD648
|
91.7
|
°C
|
|
热变形温度4(1.8MPa,未退火,64.0mm跨距)
|
|
ISO75-2/Af
|
93.4
|
°C
|
|
线形热膨胀系数-流动(-40到40°C)
|
|
ASTME831
|
8.9E-5
|
cm/cm/°C
|
|
线形热膨胀系数-横向(-40到40°C)
|
|
ASTME831
|
8.5E-5
|
cm/cm/°C
|