性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
物理性能
|
比重
|
|
ASTMD792
|
1.20
|
g/cm3
|
|
特定体积
|
|
ASTMD792
|
0.835
|
cm3/g
|
|
密度
|
|
ASTMD792
|
1.19
|
g/cm3
|
|
熔流率（熔体流动速率）(300°C/1.2kg)
|
|
ASTMD1238
|
18
|
g/10min
|
|
收缩率-流动(3.20mm)
|
|
InternalMethod
|
0.50to0.70
|
%
|
|
吸水率(24hr)
|
|
ASTMD570
|
0.15
|
%
|
|
吸水率
|
平衡,23°C
|
ASTMD570
|
0.35
|
%
|
|
平衡,100°C
|
ASTMD570
|
0.58
|
%
|
|
室外适用性
|
|
UL746C
|
f2
|
|
|
机械性能
|
抗张强度2(屈服)
|
|
ASTMD638
|
62.1
|
MPa
|
|
抗张强度2(断裂)
|
|
ASTMD638
|
68.9
|
MPa
|
|
伸长率2(屈服)
|
|
ASTMD638
|
7.0
|
%
|
|
伸长率2(断裂)
|
|
ASTMD638
|
130
|
%
|
|
弯曲模量4(50.0mm跨距)
|
|
ASTMD790
|
2340
|
MPa
|
|
弯曲强度4(屈服,50.0mm跨距)
|
|
ASTMD790
|
96.5
|
MPa
|
|
泰伯耐磨性(1000Cycles,1000g,CS-17转轮)
|
|
ASTMD1044
|
10.0
|
mg
|
|
冲击性能
|
简支梁缺口冲击强度4
|
-30°C
|
ISO179/1eA
|
12
|
kJ/m2
|
|
23°C
|
ISO179/1eA
|
65
|
kJ/m2
|
|
简支梁无缺口冲击强度4
|
-30°C
|
ISO179/1eU
|
NoBreak
|
|
|
23°C
|
ISO179/1eU
|
NoBreak
|
|
|
悬壁梁缺口冲击强度(23°C)
|
|
ASTMD256
|
690
|
J/m
|
|
悬壁梁缺口冲击强度5
|
-30°C
|
ISO180/1A
|
11
|
kJ/m2
|
|
23°C
|
ISO180/1A
|
65
|
kJ/m2
|
|
悬壁梁缺口冲击强度(23°C)
|
|
ASTMD4812
|
3200
|
J/m
|
|
无缺口伊佐德冲击强度5
|
-30°C
|
ISO180/1U
|
NoBreak
|
|
|
23°C
|
ISO180/1U
|
NoBreak
|
|
|
装有测量仪表的落镖冲击(23°C,EnergyatPeakLoad)
|
|
ASTMD3763
|
62.1
|
J
|
|
落锤冲击(23°C)
|
|
ASTMD3029
|
169
|
J
|
|
拉伸冲击强度6
|
|
ASTMD1822
|
546
|
kJ/m2
|
|
硬度
|
洛氏硬度
|
M计秤
|
ASTMD785
|
70
|
|
|
R计秤
|
ASTMD785
|
118
|
|
|
热性能
|
载荷下热变形温度(0.45MPa,未退火,6.40mm)
|
|
ASTMD648
|
138
|
°C
|
|
载荷下热变形温度(1.8MPa,未退火,6.40mm)
|
|
ASTMD648
|
129
|
°C
|
|
维卡软化温度
|
|
ASTMD15257
|
154
|
°C
|
|
线形热膨胀系数-流动(-40到95°C)
|
|
ASTME831
|
6.8E-5
|
cm/cm/°C
|
|
比热
|
|
ASTMC351
|
1260
|
J/kg/°C
|
|
导热系数
|
|
ASTMC177
|
0.25
|
W/m/K
|
|
RTIElec
|
|
UL746
|
130
|
°C
|
|
RTIImp
|
|
UL746
|
130
|
°C
|
|
RTIStr
|
|
UL746
|
130
|
°C
|
|
电气性能
|
体积电阻率
|
|
ASTMD257
|
>1.0E+17
|
ohms·cm
|
|
介电强度(3.20mm,inAir)
|
|
ASTMD149
|
15
|
kV/mm
|
|
介电常数
|
50Hz
|
ASTMD150
|
3.17
|
|
|
60Hz
|
ASTMD150
|
3.17
|
|
|
1MHz
|
ASTMD150
|
2.96
|
|
|
耗散因数
|
50Hz
|
ASTMD150
|
9.0E-4
|
|
|
60Hz
|
ASTMD150
|
9.0E-4
|
|
|
1MHz
|
ASTMD150
|
0.010
|
|
|
相比耐漏电起痕指数(CTI)
|
|
UL746
|
PLC2
|
|
|
高电弧燃烧指数(HAI)
|
|
UL746
|
PLC1
|
|
|
高电压电弧起痕速率(HVTR)
|
|
UL746
|
PLC2
|
|
|
热丝引燃(HWI)
|
|
UL746
|
PLC2
|
|
|
可燃性
|
UL阻燃等级(0.70mm)
|
|
UL94
|
HB
|
|
|
RadiantPanelListing(UL)
|
|
|
YES
|
|
|
光学性能
|
折射率
|
|
ASTMD542
|
1.586
|
|
|
透射率(2540μm)
|
|
ASTMD1003
|
88.0
|
%
|
|
雾度(2540μm)
|
|
ASTMD1003
|
1.0
|
%
|